Tin powder and auxiliary composition
SMT manufacturing relies on quality solder paste printing. Many factors affect the quality of solder paste’s printing. It is important to know the properties of solder dust and how much solder powder you have to make solder paste melt. This will also affect the printing speed, printability, weldability, and quality of the solder joints. The eutectic temperature of tin powder-alloy components should be as close as possible to the eutectic. It is calculated as the proportion of flux and tin in paste. Tin powder content directly influences the viscosity, printing and durability of solder paste. In general, the content of tin powder is 7590%. Tin powder is 75 to 90% in general. It is used for template printing and no-cleaning solder paste. The content of the tin used in drip coating is 75 to 85 p>
The size, shape and distribution of the Tin powder particles
It is important to consider the size, shape, and uniformity of the tin powder particles in order to influence the properties. It is best to use smaller particles for solder paste printing, particularly when using high density products that have a narrow spacing. About 1/5th of the opening size for a template is used to measure the particle diameter. While the pattern of solder paste printed with small particles alloy powder is very detailed, edge collapse can easily be caused by it. The potential for oxidation is greater due to small particles’ large surfaces. If the assembly density of the powder is low, it’s possible to choose a coarser alloy powder without having an impact on the printing ability. This can improve both the weldability as well as reduce the price for solder paste. Also, the form of the alloy powder can impact the paste’s printingability and desorption as well as weldability. Spherical-particle alloy paste has good printing properties, low viscosity and easy to collapse after printing. This makes it ideal for printing metal templates and narrow spacing screens. Because of their small size, high oxygen content, and bright welding spots, spherical particle alloy powder improves welding quality. At present, however, they are mostly used.
Solder paste, a fluid that is highly thixotropic can be made to flow by external forces. It is the most important characteristic of solder paste. Viscosity can affect the performance of printing. Viscosity determines how easy it will be to get out of the template. The percentage of tin in the paste also influences the viscosity. A large percentage of flux indicates a lower viscosity.
Biomedicalmaterialsprogram (aka. Biomedicalmaterialsprogram is an advanced material. With over 12 years of experience, Biomedicalmaterialsprogram is an established global supplier and manufacturer for chemical materials. High quality Tin Powder are produced by our company. We can help you if the price is lower.